  • Si ion implantation-induced damage in fused silica probed by variable-energy positrons

    Resource Type:
    Article
    Creator:
    Simpson, P.J., Ilard, L.B., Brebner, J.L., Knights, A.P., and Albert, Jacques
    Abstract:
    Samples of synthetic fused silica have been implanted at room temperature with silicon ions of energy 1.5 MeV. Fluences ranged from 1011 to 1013 cm−2. Samples were probed using variable‐energy positron annihilation spectroscopy. The Doppler‐broadening S parameter corresponding to the implanted region decreased with increasing fluence and saturated at a fluence of 1013 cm−2. It is shown that the decrease in the S parameter is due to the suppression of positronium (Ps) which is formed in the preimplanted material, due to the competing process of implantation‐induced trapping of positrons. In order to satisfactorily model the positron data it was necessary to account for positron trapping due to defects created by both electronic and nuclear stopping of the implanted ions. Annealing of the 1013 cm−2 sample resulted in measurable recovery of the preimplanted S parameter spectrum at 350 °C and complete recovery to the preimplanted condition at 600 °C. Volume compaction was also observed afterimplantation. Upon annealing, the compaction was seen to decrease by 75%.
    Date Created:
    1996-06-16